The First (“Heroic”) Experiments to Generate Light From Organic Materials:Top and Bottom Electrodes/Rectifying Junctions

The first experiments to generate light from organic materials were conducted in the late 1950s and early 1960’s at places like RCA. These studies were driven by the hypothesis that organic materials would act as efficient light sources and would also serve as organic photoconductors.

See Helfrich [1]

Scientists used fine slices of highly purified anthracene (C<sub14>H<sub10>), approximately 5mm thick, connect them to electrodes, and apply 100-1000 volts. If the system did not short there would be faint blue light emission. Often there would be a lightning bolt-like discharge and graphite was produced instead of light. The high voltages were needed to overcome the internal resistance to charge migration (Rs) in the organic solid. The relatively large thickness of these slices was an experimental necessity – pin-hole-free ultrathin film deposition technology was not yet available for organic materials. Emission was seen occurring near the cathode, suggesting that charge recombination occurred closer to this electrode than the center of the device.

<embed_document width="55%" height="400">http://depts.washington.edu/cmditr/media/OLED4_firstexperiments.pdf</embed_document>

Subsequent experiments used thinner slices of anthracene (50 microns) with a semitransparent gold electrode and a silver paste cathode. Lower drive voltages were required, and light emission through the semitransparent anode was observed. Despite the relatively high external quantum efficiency of these devices, it was clear that substantial materials development would be necessary before real display devices would be realized. The cited review by Dresner shows a substantial understanding of the physics of these light emitting organic thin films, which extrapolates directly to our understanding of OLEDs today.

See Dresner [2]

How is Light Generated?

  • Electrons are removed at the anode, creating a cation radical state.
  • Electrons are added at the cathode, creating the anion radical state.
  • These charges move through the organic crystal, and meet each other near the center of the device.
  • An electron transfer between the reduced donor and the oxidized acceptor takes place.
  • Enough excess free energy is generated to create the emissive state of anthracene, thus light is emitted.

In these early devices, the rate of transport of the positive cation radical (or hole state) and the transport of the electron rich state were not equal, causing the recombination to occur near one of the contact electrodes. This phenomenon is now known to inhibit device effiency.


The First Practical OLEDs

OLED4 heterojunction.jpg

The first practical OLEDs were built in the late 1980’s by Ching Tang and Andy Van Slyke at Kodak. This was a revolution for the technology.

C.W. Tang and coworkers at Kodak used spin casting and sublimation deposition of the organic components of the device, with patterned electrodes on the top and bottom. This was an important technological advance over slicing single-crystal anthracene as thin as possible with a razor knife. Vapor depositing molecules in a vacuum system on top of a transparent conductor enabled the layers to be much thinner, and have almost none of the pinholes that cause shorts. Transparent conducting oxide (TCO) thin films on glass served as the anode and allowed light to be emitted in a usable fashion for displays. The keys to successful development of these first devices was control of organic film deposition to create a pin-hole free film (with high RP) which was thin enough to yield a lower series resistance than the first anthracene devices, providing for light emission with drive voltages under 50 volts. The hole transparent layer was a spin coated polymer. This produced about 15 candelas per square meter, which is a dim but visible light. (A typical CRT computer screen operates with 100-200 candelas per square meter.)

Anatomy of Early OLEDs

  • The base of the device was a glass or plastic substrate.
  • A transparent conductor such as indium tin oxide (ITO).
  • A 50 nm hole transport layer (HTL) of an easily oxidized material such as triarylamine or poly vinyl carbazol.
  • A 50 nm electron transport layer (ETL) of aluminum tris quinalate.
  • A cathode made from a metal such as aluminum, magnesium-silver alloy or even calcium.

See Tang C.W. [3] [4]


  • Vacuum deposition enabled thin electron transport layer
  • Hole transport layer was spin-coated polymer: 10 – 20 V, 15cd/m2 brightness
  • All vacuum device: 10 – 20 V, 100 cd/m2 using Alq3 emission layer

References

  1. W.Helfrich & W.G. Sneider Phys. Rev. Lett. 14(7), 229 (1965)
  2. J. Dresner, RCA Rev. 30, 322 (1969)
  3. Tang and S.A. VanSlyke Appl. Phys. Lett. 51, 913(1987)
  4. C.W. Tang, U.S. Patent # 4,356,429 (1980)
Previous Topic Return to OLED Menu Next Topic